载气热提取法测定熔敷金属中扩散氢收集条件的探究

探究了GB/T 3965—2012《熔敷金属中扩散氢测定方法》中载气热提取法收集条件对测定扩散氢含量的影响,并与水银法进行了对比。研究结果表明,样本炉温设定为400℃,A型试块的内部温度大约在51 min时稳定在358℃左右,B型试块内部温度大约在27 min时稳定在391℃左右;载气热提取法电信号曲线收集结束点的电信号及斜率均接近0时获得的结果与水银法具有较好的一致性。     

Oxidation‐led decomposition of hexagonal boron nitride coatings on alloy substrates at 900 °C: Ti‐6Al‐4V

Hexagonal boron nitride (h‐BN) coatings on Ti‐6Al‐4V substrates undergo complete decomposition in air at 900 °C. This fate is similar to that of this ceramic material on chromia‐former alloys, and unlike that of a mass of powder treated in isolation. As the ceramic and alloy oxidize concurrently, outwardly diffusing aluminum (III) ions but not the predominant titanium (IV) ions react with the boron trioxide that forms around the h‐BN basal plane peripheries. Resultant aluminum borate is incorporated into the growing scale and the boron trioxide diffusion barrier is depleted. By this mechanism, the oxidation of h‐BN is maintained at an enhanced rate, until both this material and its oxide completely decompose. Liberated nitrogen from the oxidation of h‐BN can enter the underlying scale as a randomly distributed solute in rutile solid solution. The post‐coating oxide‐atmosphere interface comprises elongated aluminum borate crystallites protruding through at the boundaries between 3–5 at% nitrogen‐doped rutile grains. It differs significantly from that of oxidized, uncoated Ti‐6Al‐4V, which is occupied by a thin α‐alumina layer atop rutile. This interface does not change with an additional 72 h of heat‐treatment.     

罩式退火温度对高强IF钢组织及性能的影响

为研究不同退火温度下高强IF钢的组织性能及织构的变化规律,采用温箱式电阻炉加热模拟罩式退火工艺,研究了不同退火温度下高强IF钢210P1冷轧板力学性能;对不同退火温度钢板的r90进行了统计并对其进行显微组织观察;采用X射线衍射仪及热场发射扫描电镜对不同退火温度的罩式退火成品板进行了织构分析。结果表明,在高强IF钢210P1冷轧板的罩式退火过程中,提高退火温度将使晶粒明显长大。随着退火温度的升高,屈服强度及抗拉强度下降,伸长率升高,n值略有上升,板材横向r值增加较明显,有利织构{111}取向密度增加,不利织构{100}取向密度降低。     

迁钢210 t钢包全程加盖工艺及实践

迁钢二炼钢厂自投入使用210 t钢包全程加盖技术及工艺后，取得了显著效果，平均出钢温度降低10 ℃，钢包热周转使用率长期保持在85%以上，取消了钢包在线烘烤，降低了煤气消耗，有效地保证了钢包洁净度，提高了钢包包衬寿命。实践生产运行表明，炼钢生产中钢包全程加盖工艺是一项节能、环保、降耗的先进技术，为迁钢二炼钢厂取得了显著的经济效益。但在一段时间内，该工艺运行稳定性较差，通过现场生产数据归纳分析，从中找出了影响钢包加、揭盖的因素，并制定了控制措施；同时，岗位要掌握其操作要点及主要设备，才能提高运行稳定性。     

Microstructure and flexural strength of the Y:TZP/BG composite

The addition of bioactive glasses to a Y:TZP matrix represents a feasible alternative to provide bioactivity to this material and optimize osseointegration. This work evaluated the effect of the BG concentration (0 and 10 wt%) and the sintering temperature (1200°C and 1300°C) on the microstructure, relative density, and flexural strength of the composite Y:TZP/BG. The Y:TZP and Y:TZP/BG powders were uniaxially pressed and sintered at 1200°C or 1300°C for 1 h. The microstructure was characterized by X-ray diffraction analysis, scanning electron microscopy, and energy-dispersive X-ray Spectroscopy. Relative density was calculated from density values obtained using the Archimedes’ principle. For the flexural strength, specimens (n = 6) were fractured in a biaxial flexural setup using a piston-on-three-balls fixture in a universal testing machine. Bioactivity test was performed in simulated body fluid solution. The results suggested that BG addition decreased the grain size of the composite, increased porosity and caused a significant decrease in the relative density and flexural strength. Crystalline phases of calcium stabilized cubic zirconia and sodium zirconium silicate were formed after the addition of BG. Finally, it was concluded that composite specimens sintered at 1300°C showed the highest density values and larger grains compared to those sintered at 1200°C.     

钢包包衬侵蚀对内衬温度和钢水温降的影响

为了研究包衬侵蚀对钢水温降的影响规律,通过ANSYS有限元软件以及ParaMesh网格随移技术建立了考虑包衬侵蚀的钢包传热计算模型,研究并分析了包衬侵蚀对包衬及钢水温度的影响规律。结果表明,包衬侵蚀对包衬温度影响较大,在相邻两个修包周期内,包衬侵蚀造成渣线和包壁的包衬内部(工作层与永久层交界处)温差为14～114 K;包衬侵蚀导致包壳外表面温度升高,包壳向外散热增加,与此同时,包衬受侵蚀变薄,蓄热减少,两者同时作用导致包衬侵蚀对钢水温降影响不大,最高不超过1 K,在实际生产中可以适当地忽略钢包侵蚀对钢水温降的影响。     

Near‐Infrared (NIR) Organic Light‐Emitting Diodes (OLEDs): Challenges and Opportunities

The rapid development of the science and technology of organic semiconductors has already led to mass application of organic light‐emitting diodes (OLEDs) in television monitors of outstanding quality as well as in a large variety of smaller displays found in smartphones, tablets, and other gadgets, while introduction of the technology to the illumination sector is imminent. Notably, the requirements of all such applications for emission in the visible range of the electromagnetic spectrum are well tuned to the optical and electronic properties of typical organic semiconductors, thereby representing relatively “low‐hanging fruits,” in terms of material development and exploitation. However, the question arises as to whether developing materials suited for efficient near‐infrared (NIR, 700–1000 nm) emission is possible, and, crucially, desirable to enable new classes of applications spanning from through‐space, short‐range communications to biomedical sensors, night vision, and more generally security applications to name but a few. Here, the major fundamental hurdles to be overcome to achieve efficient NIR emission from organic π‐conjugated systems are discussed, recent progress is reviewed, and an outlook for further development of both materials and applications is provided.     

硬质道路石油沥青关键组分的研制

筛选出适合制备硬质道路石油沥青关键组分的减压渣油，并以此为原料，考察了蒸馏深拔、深度氧化及溶剂脱沥青工艺制备的硬质道路沥青关键组分的性能。所制备的关键组分能够大幅提升基质沥青的高温性能，且通用性好；将关键组分与基质沥青按适合比例调合可以稳定生产高温性能好的硬质道路石油沥青，其混合料耐高温性能好。同时,为便于硬质沥青关键组分的使用,还开发了关键组分的造粒成型技术,提出其适于成型造粒的黏度范围为0.6～6 Pa?S。采用关键组分生产的硬质道路沥青用于高速公路实体工程，经过2年以上的气候和通车考验，沥青路面无车辙、无开裂，保持优良的使用性能。